Influence of Ag Photodeposition Conditions over SERS Intensity of Ag/ZnO Microspheres for Nanomolar Detection of Methylene Blue.

Surface enhanced Raman spectroscopy (SERS) is considered a versatile and multifunctional technique with the ability to detect molecules of different species at very low molar concentration. In this work, hierarchical ZnO microspheres (ZnO MSs) and Ag/ZnO MSs were fabricated and decorated by hydrothermal and photodeposition methods, respectively. For Ag deposition, precursor molar concentration (1.9 and 9.8 mM) and UV irradiation time (5, 15, and 30 min) were evaluated by SEM, TEM, X-ray diffraction and Raman spectroscopy. X-ray diffraction showed a peak at 37.9° corresponding to the (111) plane of Ag, whose intensity increases as precursor concentration and UV irradiation time increases. SEM images confirmed the formation of ZnO MSs (from 2.5 to 4.5 µm) building by radially aligned two-dimensional ZnO nanosheets with thicknesses below 30 nm. The Raman spectra of Ag/ZnO MSs exhibited a vibration mode at 486 cm-1 which can be directly associated to Ag deposition on ZnO MSs surface. The performance of SERS substrate was evaluated using rhodamine 6G. The SERS substrate grown at 9.8 mM during 30 min showed the best SERS activity and the ability to detect methylene blue at 10-9 M.

Estudio comparativo de la bioactividad de dos materiales biocerámicos / Comparative Study of the Bioactivity of Two Bioceramic Materials

RESUMEN Los materiales a base de silicato de calcio han demostrado ser bioactivos debido a su capacidad para producir apatita carbonatada biológicamente compatible. El objetivo de este estudio fue analizar la bioactividad de Biodentine™ y MTA Repair HP® en contacto con discos de dentina humana, que se obturaron y dividieron aleatoriamente para formar cuatro grupos: grupo 1 Biodentine™, grupo 2 MTA Repair HP®, grupo control positivo MTA Angelus® y grupo control negativo IRM®, los cuales se incubaron en solución PBS durante 10 días, para posterior análisis por medio de MEB-EDS y Espectroscopía Raman. Los tres materiales a base de silicato de calcio analizados en este estudio demostraron ser bioactivos pues al entrar en contacto con una solución a base de fosfato desencadenaron la precipitación inicial de fosfato de calcio amorfo, que actúa como precursor durante la formación de apatita carbonatada.

ABSTRACT Calcium silicate-based materials have been shown to be bioactive due to their ability to produce biologically compatible carbonated apatite. The objective of this study was to analyze the bioactivity of Biodentine ™ and MTA Repair HP® in contact with human dentine discs, which were sealed and divided randomly to form four groups: group 1 Biodentine™, group 2 MTA Repair HP®, positive control group MTA Angelus® and negative control group IRM®, which were incubated in PBS solution for 10 days, for a subsequent analysis by means of MEB-EDS and Raman spectroscopy. The three calcium-based materials analyzed in this study proved to be bioactive because upon contact with a phosphate-based solution they were triggered at the onset of amorphous calcium phosphate, as the precursor during the formation of carbonated apatite.

Cytotoxicity Evaluation of Anatase and Rutile TiO2 Thin Films on CHO-K1 Cells in Vitro.

Cytotoxicity of titanium dioxide (TiO2) thin films on Chinese hamster ovary (CHO-K1) cells was evaluated after 24, 48 and 72 h of culture. The TiO2 thin films were deposited using direct current magnetron sputtering. These films were post-deposition annealed at different temperatures (300, 500 and 800 °C) toward the anatase to rutile phase transformation. The root-mean-square (RMS) surface roughness of TiO2 films went from 2.8 to 8.08 nm when the annealing temperature was increased from 300 to 800 °C. Field emission scanning electron microscopy (FESEM) results showed that the TiO2 films' thickness values fell within the nanometer range (290-310 nm). Based on the results of the tetrazolium dye and trypan blue assays, we found that TiO2 thin films showed no cytotoxicity after the aforementioned culture times at which cell viability was greater than 98%. Independently of the annealing temperature of the TiO2 thin films, the number of CHO-K1 cells on the control substrate and on all TiO2 thin films was greater after 48 or 72 h than it was after 24 h; the highest cell survival rate was observed in TiO2 films annealed at 800 °C. These results indicate that TiO2 thin films do not affect mitochondrial function and proliferation of CHO-K1 cells, and back up the use of TiO2 thin films in biomedical science.

Biocompatibility and Surface Properties of TiO2 Thin Films Deposited by DC Magnetron Sputtering.

We present the study of the biocompatibility and surface properties of titanium dioxide (TiO2) thin films deposited by direct current magnetron sputtering. These films are deposited on a quartz substrate at room temperature and annealed with different temperatures (100, 300, 500, 800 and 1100 °C). The biocompatibility of the TiO2 thin films is analyzed using primary cultures of dorsal root ganglion (DRG) of Wistar rats, whose neurons are incubated on the TiO2 thin films and on a control substrate during 18 to 24 h. These neurons are activated by electrical stimuli and its ionic currents and action potential activity recorded. Through X-ray diffraction (XRD), the surface of TiO2 thin films showed a good quality, homogeneity and roughness. The XRD results showed the anatase to rutile phase transition in TiO2 thin films at temperatures between 500 and 1100 °C. This phase had a grain size from 15 to 38 nm, which allowed a suitable structural and crystal phase stability of the TiO2 thin films for low and high temperature. The biocompatibility experiments of these films indicated that they were appropriated for culture of living neurons which displayed normal electrical behavior.